Taflen ddata incoloy 800
1. Gwybodaeth Gyffredinol
Gradd:Incoloy 800 (UNS N08800)
Math:Aloi nicel-haearn-cromiwm
Safonau:ASTM B407, B409, B163, ASME SB -163, sb -409
2. Cyfansoddiad cemegol (wt.%)
| Elfen | Mini | Max |
|---|---|---|
| Nicel (Ni) | 30.0 | 35.0 |
| Cromiwm (cr) | 19.0 | 23.0 |
| Haearn | Mantolwch | - |
| Carbon (c) | - | 0.10 |
| Manganîs (mn) | - | 1.00 |
| Silicon (Si) | - | 1.00 |
| Titaniwm (TI) | 0.15 | 0.60 |
| Alwminiwm | 0.15 | 0.60 |
3. Priodweddau mecanyddol
| Eiddo | Gwerth nodweddiadol |
|---|---|
| Cryfder tynnol | 515 - 690 MPa (75–100 ksi) |
| Cryfder cynnyrch (0. 2%) | 205 - 310 MPa (30–45 ksi) |
| Hehangu | Yn fwy na neu'n hafal i 30% |
| Caledwch | 170 - 210 HB |
| Modwlws o hydwythedd | ~ 200 GPA (29, 000 ksi) |
4. Priodweddau Ffisegol
| Eiddo | Gwerthfawrogom |
|---|---|
| Ddwysedd | 8. 0 g\/cm³ |
| Ystod doddi | 1370 - 1425 gradd |
| Dargludedd thermol | ~ 11.4 w\/m · k (100 gradd) |
| Cyfernod ehangu thermol | 13.1 µm\/m · gradd (20–100 gradd) |
5. Terfynau Tymheredd
| Hamgylchedd | Uchafswm tymheredd y gwasanaeth |
|---|---|
| Ocsideiddio atmosfferau | Hyd at 1100 gradd (gradd F) |
| Lleihau neu carburizing | Is, yn dibynnu ar amodau |
6. Gwrthiant cyrydiad
Ymwrthedd rhagorol i ocsidiad a charburization.
Yn sefydlog mewn amgylcheddau ocsideiddio a lleihau ysgafn.
Gwrthsefyll dyodiad carbid oherwydd sefydlogwyr titaniwm a alwminiwm.
7. Ceisiadau
Cyfnewidwyr gwres
Cydrannau ffwrnais
Prosesu cemegol a phetrocemegol
Cydrannau adweithydd niwclear
Elfennau gwresogi